Highest Strength And Hardness Beryllium Copper Cube2(C17200)
Beryllium Copper Sheet
Product Normal Description:
Product Name: High strength and hardness beryllium copper sheet
Grade: CuBe2(C17200)
Standard: ASTM B194
Product Size: Thickness 1mm-5mm; Max width: 300mm; Max length: 2m;
or custom diameter
State: A(TB00), H(TD04), AT(TF00), HT(TH04)
Typical Application: Electrical Industry and Industrial
Product Brand: CUBERYLLIUM®
Product Informance of Beryllium Copper CuBe2 (C17200):
C17200 beryllium copper is the most commonly asked for of CuBe
alloys. Also known as Alloy 25 or RWMA Class 4, this alloy is
capable of reaching the highest strength and hardness of all the
copper alloys.
We supply C17200 in a variety of forms including Bar and Rod (ASTM
B196), Strip, Wire, Cut Plate, Sheet, and Tube.
Chemical Composition of Beryllium Copper Cube2(C17200) Alloy:
Product Grade: CUBERYLLIUM ®-172(UNS. C17200)
Beryllium(Be): 1.80-2.00%
Cobalt(Co) + Nickel(Ni): 0.20% Min
Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max
Lead: 0.02% Max
Copper(Cu): Balance
Note: Copper plus additions equal 99.5% Minimum.
Typical Physical Properties of Beryllium Copper Cube2(C17200) Alloy:
| Density (g/cm3): | 8.36 |
| Density before age hardening (g/cm3): | 8.25 |
| Elastic Modulus (kg/mm2 (103)): | 13.4 |
| Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): | 17 x 10-6 |
| Thermal Conductivity (cal/(cm-s-°C)): | 0.25 |
| Melting Range (°C): | 870-980 |
Temper Designations of Beryllium Copper Cube2(C17200) Sheet:
| Mechanical and Electrical Properties of C17200 Sheet/Plate |
| CUBERYLLIUM | ASTM | Heat Treatment | Thickness (mm) | Tensile Strength (Mpa) | Elongation Percent | HARDNESS Rockwell B or C Scale | Electrical Conductivity
(% IACS) |
| Designation | Designation |
| A | TB00 | | All Size | 400~580 | 20~60 | B45-85 | 15～19 |
| H | TD04 | ＜10 | 600~880 | 8~20 | B91-103 | 15～19 |
| 10~25 | 600~850 | 8~20 | B90-102 | 15 ~ 19 |
| 25~50 | 580~820 | 8~20 | B88-102 | 15 ~19 |
| ＞50 | 580~820 | 8~20 | B88-102 | 15 ~19 |
| AT | TF00 |
3 hr 315℃
| All Size | 1120~1358 | 3~10 | C36-41 | 22 ~ 28 |
| HT | TH04 | 2 hr 315℃ | ＜10 | 1200~1450 | 1~5 | C38-45 | 22 ~ 28 |
| 10~25 | 1200~1500 | 1~5 | C38-44 | 22 ~ 28 |
| 25~50 | 1200~1450 | 2~5 | C37-43 | 22 ~ 28 |
| ＞50 | 1100~1350 | 2~5 | C36-42 | 22 ~ 28 |
Applications of Beryllium Copper Cube2(C17200) Alloy:
Applications for beryllium copper C17200 include electrical
components and connectors, offshore and marine, powertrains,
robotic welding and oifield tooling. The non-magnetic nature of the
alloy makes it ideal for use on down-hole wireline tools.
•Electrical/electronic connectors
•Current-carrying springs
•Precision screw machined parts
•Welding electrodes
•Bearings
•Plastic molds
•Corrosion resistant components
Product Photos:
The most important Technology of CUBERYLLIUM ®
A: Heat treatment
Heat treatment is the most important process for this alloy system.
While all copper alloys are hardenable by cold working, beryllium
copper is unique in being hardenable by a simple low temperature
thermal treatment. It involves two basic steps. The first is called
solution annealing and the second, precipitation or age hardening.
B: Solution Annealing
For the typical alloy CuBe1.9 (1.8- 2%) the alloy is heated between
720°C and 860°C. At this point the contained beryllium is
essentially “dissolved” in the copper matrix (alpha phase). By
rapidly quenching to room temperature this solid solution structure
is retained. The material at this stage is very soft and ductile
and can be readily cold worked by drawing, forming rolling, or cold
heading. The solution annealing operation is part of the process at
the mill and is not typically used by the customer. Temperature,
time at temperature, quench rate, grain size, and hardness are all
very critical parameters and are tightly controlled by ohmalloy.
C: Age Hardening
Age hardening significantly enhances the material’s strength. This
reaction is generally carried out at temperatures between 260°C and
540°C depending on alloy and desired characteristics. This cycle
causes the dissolved beryllium to precipitate as a beryllium rich
(gamma) phase in the matrix and at the grain boundaries. It is the
formation of this precipitate which causes the large increase in
material strength. The level of mechanical properties attained is
determined by the temperature and time at temperature. It should be
recognized that beryllium copper has no room temperature aging
characteristics.
Size Available
FAQ:
Q1:Could you produce Beryllium Copper strip by Mill Hardened
process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06)
XHMS(TM08).,we are the only factory could do harden strip in China.
Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous
Furnace.
3:Surface further polishing for top clients.
Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation,
Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the
amount is different.